OPTIMASI GREEN SYNTHESIS NANOKATALIS FeNi/TiO2 MENGGUNAKAN EKSTRAK KULIT MANGGIS DAN EKSTRAK BIJI ANGGUR UNTUK DEGRADASI METHYLENE BLUE

SABRINA PUTRI NURLIAN / 14-2021-012 - Personal Name
NAJLA SEPTARIANI / 14-2021-013 - Personal Name
0421057105 - Dr.rer.Nat. Riny Yolandha Parapat, S.T., M.T., M.Sc. - Personal Name
Text English 2025 Teknik Kimia : FTI

Nanoteknologi berkembang pesat dalam rekayasa material, termasuk nanokatalis yang berfungsi sebagai katalis dalam reaksi kimia. Penelitian ini menyintesis nanokatalis FeNi/TiO₂ menggunakan metode green synthesis dengan ekstrak biji anggur (GSE) dan ekstrak kulit manggis (MPE) sebagai agen pereduksi alami. Methylene blue, menjadi salah satu senyawa pewarna yang sering dipergunakan dalam bidang kimia dipilih sebagai model polutan untuk menguji efektivitas degradasi katalitik. Hasil penelitian menunjukkan bahwa nanokatalis FeNi/TiO₂ berbasis GSE memiliki Yield lebih tinggi 43,56% dibandingkan MPE 36,20% serta menunjukkan aktivitas katalitik lebih besar yakni masing – masing 12335 μmol /(L.min.gFeNi) dan 7973 μmol /(L.min.gFeNi). Hal ini disebabkan oleh kandungan polifenol, tanin, dan flavonoid yang lebih tinggi pada GSE, yang menghasilkan nanopartikel dengan ukuran lebih kecil dan distribusi lebih merata. Faktor utama yang mempengaruhi Yield ialah jumlah support TiO₂, sedangkan aktivitas katalitik dipengaruhi oleh waktu reaksi pada GSE dan jumlah logam dalam precursor pada MPE. Optimasi sintesis menunjukkan bahwa kondisi terbaik untuk MPE diperoleh pada jumlah logam FeNi 75 mg, pereduksi 36 mg, jumlah support TiO₂ 2,40 g, dan waktu reaksi 1 jam, menghasilkan Yield 40,05% dan aktivitas 15.880 μmol./L.min.g FeNi. Sementara itu, kondisi optimal untuk GSE diperoleh pada jumlah logam FeNi 12 mg, pereduksi 150 mg, support TiO₂ 2 g, dan waktu reaksi 1 jam, menghasilkan Yield 77,29% dan aktivitas 30.680 μmol./L.min.gFeNi. Validasi eksperimen menunjukkan bahwa penyimpangan antara hasil optimasi teoritis dan eksperimen relatif kecil, yaitu 0,799% dan 20,98% untuk MPE, serta 0,4% dan 0,15% untuk GSE. Dengan demikian, ekstrak biji anggur terbukti lebih efektif dalam meningkatkan Yield dan aktivitas katalitik dibandingkan ekstrak kulit manggis.

Nanotechnology has advanced rapidly in material engineering, including the development of nanocatalysts that function as catalysts in chemical reactions. This study focused on the synthesis of FeNi/TiO₂ nanocatalysts using a green synthesis method with grape seed extract (GSE) and mangosteen peel extract (MPE) as natural reducing agents. Methylene blue, a commonly used dye in chemistry, served as a model pollutant to evaluate catalytic degradation effectiveness. The findings revealed that FeNi/TiO₂ nanocatalysts synthesized with GSE achieved a higher Yield of 43.56% compared to MPE at 36.20%, along with greater catalytic activity of 12.335 μmol/(L.min.gFeNi) and 7.973 μmol/(L.min.gFeNi), respectively. The superior performance of GSE resulted from its higher content of polyphenols, tannins, and flavonoids, which produced smaller nanoparticles with a more uniform distribution. The primary factor influencing Yield involved the amount of TiO₂ support, whereas catalytic activity depended on reaction time for GSE and metal precursor concentration for MPE. Optimization results indicated that the best conditions for MPE included 75 mg FeNi metal, 36 mg reducing agent, 2.40 g TiO₂ support, and a reaction time of 1 hour, Yielding 40.05% with a catalytic activity of 15,880 μmol./L.min.g FeNi. Meanwhile, optimal conditions for GSE included 12 mg FeNi metal, 150 mg reducing agent, 2 g TiO₂ support, and a reaction time of 1 hour, Yielding 77.29% and a catalytic activity of 30,680 μmol./L.min.g FeNi. Experimental validation demonstrated minimal deviations between theoretical optimization and experimental results, with 0.799% and 20.98% for MPE, and 0.4% and 0.15% for GSE. These results confirmed that grape seed extract enhanced Yield and catalytic activity more effectively than mangosteen peel extract.

Ketersediaan

LOADING LIST...

Lampiran Berkas

LOADING LIST...

Detail Information

Bagian	Informasi
Pengarang	SABRINA PUTRI NURLIAN / 14-2021-012 - Personal Name NAJLA SEPTARIANI / 14-2021-013 - Personal Name 0421057105 - Dr.rer.Nat. Riny Yolandha Parapat, S.T., M.T., M.Sc. - Personal Name
No. Panggil	709TK/25
Subyek	Nanoteknologi, Nanokatalis, Methylene Blue (MB) Biji Anggur, Kulit Manggis
Fakultas	FTI
Tahun Terbit	2025
Jurusan	Teknik Kimia
Deskripsi Fisik
Info Detil Spesifik

Citation

APA Style

. (2025).OPTIMASI GREEN SYNTHESIS NANOKATALIS FeNi/TiO2 MENGGUNAKAN EKSTRAK KULIT MANGGIS DAN EKSTRAK BIJI ANGGUR UNTUK DEGRADASI METHYLENE BLUE().Teknik Kimia:FTI

Chicago Style

.OPTIMASI GREEN SYNTHESIS NANOKATALIS FeNi/TiO2 MENGGUNAKAN EKSTRAK KULIT MANGGIS DAN EKSTRAK BIJI ANGGUR UNTUK DEGRADASI METHYLENE BLUE().Teknik Kimia:FTI,2025.Text

MLA Style

.OPTIMASI GREEN SYNTHESIS NANOKATALIS FeNi/TiO2 MENGGUNAKAN EKSTRAK KULIT MANGGIS DAN EKSTRAK BIJI ANGGUR UNTUK DEGRADASI METHYLENE BLUE().Teknik Kimia:FTI,2025.Text

Turabian Style

.OPTIMASI GREEN SYNTHESIS NANOKATALIS FeNi/TiO2 MENGGUNAKAN EKSTRAK KULIT MANGGIS DAN EKSTRAK BIJI ANGGUR UNTUK DEGRADASI METHYLENE BLUE().Teknik Kimia:FTI,2025.Text

Detail Cantuman

OPTIMASI GREEN SYNTHESIS NANOKATALIS FeNi/TiO2 MENGGUNAKAN EKSTRAK KULIT MANGGIS DAN EKSTRAK BIJI ANGGUR UNTUK DEGRADASI METHYLENE BLUE

Detail Information

Citation

Homepage Info

Koleksi

Media Sosial / Kanal

Address